Influence Of Li+ Doping On Photoluminescence Properties Of Sr5(PO4)3F:Eu3+

In this article, the influence of lithium co-doped on Sr5(PO4)3F:Eu 3+ halophosphate based phosphor reported. The Sr5(PO4)3F:Eu 3+ and Sr5(PO4)3F:Eu 3+ , Li + phosphors were prepared by combustion synthesis route using urea as the fuel. The phosphors were characterized by X-ray diffraction (XRD) and photoluminescence (PL) techniques. The powders were annealed at 900 o C and 1200 o C and characterized by X-ray diffraction (XRD) which shows that the major crystalline phases from the as prepared or annealed powder samples were identical. The PL results show that the incorporation of Li + ions into the Sr5 (PO4)3F:Eu 3+ lattice could induce a remarkable improvement of the PL intensity in red region at 395 nm excitation wavelength. The highest emission intensity was observed with the compound of Eu 3+ 0.5 mol% and Li + 0.5 mol% co-doped Sr5(PO4)3F, whose brightness was increased by a factor of more than 3.0 in comparison with that of the Sr5(PO4)3F:Eu 3+ . The 300–400 nm is Hg free excitati