Comparative study of structure, dielectric and electrical behavior of Ba(Fe0.5Nb0.5)O3 ceramics and their solid solutions with BaTiO3

Dielectric properties of (1-x)Ba(Fe0.5Nb0.5)O3-xBaTiO3 (where x = 0.00, 0.05 and 0.10) solid solution ceramics at high temperature range of RT ~ 270 o C have been characterized in this paper. The above said polycrystalline ceramics with (x = 0.0, 0.05 and 0.10) have been produced via a mixed oxide route. The effects of BaTiO3 substitution on the structure and on the electrical and ferroelectric properties of Ba(Fe0.5Nb0.5)O3 samples have been studied by performing x-ray diffraction and dielectric measurements. The dielectric properties (e¢ and tan d) were investigated in the temperature range of 30-270 °C and in the frequency range of 100 Hz-5 MHz. The variation of relative dielectric permittivity (tan d) and tangent loss (tan d) has suggested a significant role of hopping of trapped charge carriers, which is resulted in an extra dielectric response in addition to the dipole response. It is observed that: (i) the relative dielectric permittivity and tangent loss (tan d) are dependent o