Nanaostructured ZnO, ZnO-TiO2 And ZnO-Nb2O5 As Solid State Humidity Sensor

Present paper deals with a comparative performance of n-type ZnO, ZnO-TiO2 and ZnO-Nb2O5 nanomaterials as humidity sensors. ZnO was synthesized through hydroxide route. TiO2 and then Nb2O5 were used as additives for improvement of sensitivity. Scanning electron micrograph of ZnO shows rod-like particles with average diameter 40 nm. Structural properties by X-Ray diffraction were studied. The minimum crystallite sizes of ZnO-TiO2 and ZnO-Nb2O5 calculated from Scherrer’s formula were found to be 19 and 17 nm respectively. The pellet of each sensing material was annealed at temperatures 150, 300, 450 and 550 ?C for 3 h and checked for its sensing efficiency. Each heat treated pellet was exposed to humidity under controlled condition and variations in resistance with the humidity were recorded. Comparative study of sensitivities of each sensing element was performed. Average sensitivity achieved was 8 MΩ/%RH for the n-type ZnO annealed at 550 ?C. After chemical mixing of TiO2, the sensitiv