Structural, Dielectric And Conductivity Properties Of Ba2+ doped (Bi0.5Na0.5)TiO3 ceramic

Polycrystalline (Bi0.5Na0.5)1-xBaxTiO3 [here after BNBT], x = 0, 0.02, 0.04, 0.06, 0.08, and 0.1 ceramics have been synthesized by conventional solid state reaction process and were characterized by X-ray diffraction technique, which indicates that on substitution of Ba 2+ in Bi0.5Na0.5TiO3 (BNT) ceramic there is splitting of the (2 0 0) peak for x ≥ 0.06. This splitting in the peak position reveals that the composition BNBT-0.06 is well in Morphotropic Phase Boundary (MPB) region where rhombohedral and tetragonal phase co-exist. Scanning electron micrograph shows decrease in grain size from 0.66 to 0.53 μm with increasing concentration of Ba 2+ ; and the dielectric constant of Ba 2+ doped BNT ceramics increased with decreasing grain sizes and a maximum value was attained at size of 0.54 ~ 0.56 μm. Doped BNT ceramic also exhibit diffuse phase transition and are characterised by a strong temperature and frequency dispersion of the permittivity which would be connected with the cation di