Magnetic And Dielectric Properties Of Multiferroic BiFeO3 nanoparticles Synthesized By A Novel Citrate Combustion Method

Single phase BiFeO3 nanoparticles have been successfully synthesized for the first time by a novel citrate combustion method without using any solvent. Well mixed metal nitrates along with citric acid which is used as fuel combust to give BiFeO3 nanoparticles after annealing. These particles are single phase in nature and crystallize in the rhombohedral distorted perovskite structure (space group-R3c) which has been confirmed by the Rietveld refinement of the room temperature powder x-ray diffraction data. Nearly spherical particles of average particle size 47 nm have been seen from transmission electron micrograph. Room temperature magnetic hysteresis measurement shows weak ferromagnetism though the magnetization does not saturate upto 1.75 T applied field. The coercive field value is calculated to be 180 Oe which is 3 times higher than that prepared by solvent free combustion method using glycine. 57 Fe Mössbauer spectrum can be fitted with a sextet corresponding to single magnetic s