Photoluminescence Properties Of Eu3+, Ce3+ Doped LaPO4 Phosphors

Pure LaPO4 and LaPO4: Eu (0.5 mol %) Ce (0.5 mol %) phosphors were synthesized by the solid-state reaction method. X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FT-IR), photoluminescence (PL) spectra and the particle size analysis were used to characterize these samples. The XRD results reveal that the synthesized LaPO4:Eu (0.5 mol%) Ce (0.5 mol%) phosphors are well crystalline and assigned to the monoclinic structure with a main (120) diffraction peak. The calculated crystallite size of pure LaPO4 and LaPO4:Eu, Ce phosphors were 67.6nm and 64nm respectively. Upon excitation at 254nm wavelength, the emission spectrum of pure LaPO4 phosphor emits a maximum intensity peak at 470 (blue) nm. In the emission spectrum of LaPO4:Eu 3+ Ce 3+ phosphor, the low contributions of the red (613nm) 5D0-7F2 emissions and the high intensity of the orange-red (589nm)5D0-7F1 emission results in high color purities.The most intense emissions appearin