Structural, Dielectric And Magnetic Properties Of Nanocrystalline BaFe12O19 Hexaferrite Processed Via Sol-gel Technique

In the present work BaFe12O19 nano-hexaferrite had been synthesized by sol-gel method and then characterized for its structural, electric, dielectric and magnetic properties. X-ray diffraction studies confirmed the hexagonal structure of the prepared nanohexaferrite with no secondary phase and the particle size was found to be of the order of 49 nm. Further, the morphology of the sample has been studied by using transmission electron microscopy (TEM). A high value of the DC resistivity (5.5 × 106 Ω cm), has been obtained at room temperature. The dielectric properties such as dielectric constant (ε′), dielectric loss tangent (tan δ) and ac electrical conductivity (σac) are investigated as a function of frequency. The dielectric constant and loss tangent are found to be decreasing with the increase in frequency while ac electrical conductivity is observed to be increasing with the increase in frequency. The dielectric properties have been explained on the basis of Maxwell-Wagner’s two-la