Ion Irradiation Induced Crystallization In Iron Phosphate Glass – TEM Investigations

Iron phosphate glass (IPG) is considered as a suitable matrix for the immobilization of nuclear waste containing higher concentration of Cs, rare earth, Mo and Cr. The central issue, while disposing nuclear waste in glass matrices, is the damage in glass matrices due to the ballistic processes caused by atomic displacements due to α-particles and the recoiling of heavy nuclei resulting from actinide decay. Ion irradiation produces similar kind of damage, and hence the samples are irradiated with 4 MeV O + (self) ion. The microstructural studies were carried out using transmission electron microscopy (TEM) for as-prepared, annealed and ion irradiated samples. It is observed that ion irradiation in IPG leads to the formation of nanocrystals with different phases containing Fe, P and O. Thermally activated crystallization process is ruled out based on the non-equilibrium experimental conditions. In the present experiments, stress driven crystallization mechanism was invoked. The stress, a