Swift Heavy Ion Irradiation Induced Surface Sputtering And Micro Structural Modification Of Gold Thin Films

Two sets of gold thin films of thickness of about 20 and 50 nm, grown by thermal evaporation method on (100) silicon wafers were irradiated by 197 MeV Au ions. Grazing incidence X-Ray diffraction (GIXRD) study has been revealed lattice expansion on decreasing the film thickness. 197 MeV Au ion irradiation was not affect either the cubic crystal structure of gold or its lattice parameter. Atomic force microscopy (AFM) study indicated that the evolution of the surface morphology with ion fluence crucially depended on the film thickness, the thinner film being more sensitive than the thicker one. Irradiation led to nanoparticles formation on the surface of the films. This observation is in contrast to the generally perceived damaging role of swift heavy ion (SHI) irradiation. Power spectral density analysis of the roughness along both the lateral and vertical directions demonstrated dominance of surface diffusion over volume diffusion induced by SHI irradiation. A comparison of the sputte