Hydrothermal synthesis and electrochemical properties of MnFe2O4 nanoplates

MnFe2O4 nanoplates have been synthesized by a simple hydrothermal method. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), transmission electron microscopy (TEM), and selected area electron diffraction (SAED) have been employed to characterize the structure and morphology of the as-prepared sample. The results show that the products are plate-like morphology with 100-500 nm in length and 100-200 nm in thickness. Contrast experiments indicate that the formation of the plate-like nanostructure could be ascribed to the effect of citrate complexation. Magnetic measurements at 300 K gave the saturation magnetization and the coercive field of nanoplates 39.2 emu g -1 and 91.5 Oe, respectively. The electrochemical performance as anode material for lithium-ion batteries was further evaluated by cyclic voltammetry (CV), electrochemical impedance and charge-discharge measurements. It was demonstrated that the material could provide an initial reversible capacity of 1067 m