Influence of anodization parameters on topographic and morphological properties of TiO2 nanotube arrays: A reconstruction from SEM measurements

In this work, we fabricated samples of titanium dioxide nanotube arrays via electrochemical anodization by using titanium foils as anode and cathode. A solution of water, ethyleneglycol, and ammonium fluoride (NH4F) at room temperature was used for the samples synthesis process. Different times and anodizing voltages were used during reaction. From X-ray diffraction (XRD) and micro-diffraction (mXRD) measurements, rutile and anatase phases were identified as function of deposition parameters. The Ti3O5 phase was observed by deconvolution of Debye-Scherrer rings of the microdiffraction spectra. Annealing processes were performed for all samples in the range between 273 and 723 K, without changes in the material’s morphological properties, while the crystalline structure was affected. Nanotube diameters varying between 30 and 42 nm were observed from SEM micrographs, when NH4F concentration was changed from 0.25 to 0.50 wt%. An alternating anodizing voltage generates the formation of nan