Synthesis and thermomechanical behavior of SiC/Si compounds derived from wood waste

The traditional method of manufacturing SiC compounds is associated with a serious environmental problem, mainly due to the need for large amounts of energy (generally derived from oil) to reach processing temperatures (typically above 2500 ºC). In addition, the chemical reaction that gives rise to the formation of SiC has CO and CO2 as by-products. Therefore, in this work an alternative method to manufacture SiC/Si composites using waste from the wood industry as the main raw material was developed. SiC/Si composites were fabricated by infiltration of molten silicon into carbon preforms at 1500 °C. The carbon preforms were obtained by pyrolysis (in an inert Ar atmosphere) of four types of resin-carbon mixtures. The carbon used in the mixtures was obtained by pyrolysis of sawdust powder.