An Investigation Of Electrical, Magnetic And Optical Properties Of La1-xCaxMnO3 (x= 0.0, 0.3, 0.5 And 0.7) System

Results from a detailed investigation on the structural, optical, electrical and magnetic properties of polycrystalline bulk samples of La1-xCaxMnO3 (x=0, 0.3, 0.5 and 0.7) synthesized by solid state reaction method are presented. The Rietveld analysis of the X-Ray diffraction (XRD) profiles clearly indicated that the XRD patterns are well fitted with orthorhombic structure. Raman spectral features revealed their finger print modes and irreducible representations at the brillouin zone center as per the group theory. It is also observed that as doping is increased, these compounds tend towards a cubic form. Ooptical band gap ‘Eg’ study reveals that the Eg decreases with Ca doping resulting in increase in conductivity. This is consistent with the resistivity measurements. In all the samples, except when x = 0.0 and 0.7, the resistivity at the highest temperature measured (ρ300 K) is less than that at 5 K (ρ5K), although for temperature T