Influence Of Hollow Silica-alumina Composite Spheres Prepared Using Various Amount Of L(+)-arginine on Their Activity For Hydrolytic Dehydrogenation Of Ammonia Borane

In this work, we investigate influence of amount of L(+)-arginine on morphology of hollow silica-alumina composite spheres and their activity for hydrolytic dehydrogenation of ammonia borane. Hollow silica-alumina composite spheres were prepared by polystyrene templates method. In this method, silica-alumina composite shell were coated on polystyrene particles via a sol-gel reaction using L(+)-arginine as promoter, and the polystyrene template particles were removed by calcination. From the result of transmission electron microscopy, shell thickness of the hollow spheres prepared amount of L(+)-arginine of 0.0581, 0.1163, 0.2325, and 0.4650 g were 10, 20, 26, and 30 nm, respectively. From the result of nitrogen sorption, average pore size of the hollow spheres prepared amount of L(+)-arginine of 0.0581, 0.1163, 0.2325, and 0.4650 g was 6.2, 4.2, 3.4, and 2.9 nm, respectively. These results indicate that pore size and shell thickness changed into adjusting amount of L(+)-arginine. Activ