Influence of oxygen ions irradiation on the optical properties of photoanodes for dye sensitized solar cell

Indium Tin Oxide (ITO) coated glass acts as a substrate for photoanode of Dye Sensitized Solar Cells (DSSCs). The ITO substrate was irradiated by oxygen ion with different fluence (1x10 11 and 1x10 12 ions/cm 2 ) at 100 MeV energy. The TiO2 films were also subjected with same ion irradiation at 100 MeV of energy with fluence of 1x10 11 ions/cm 2 and 5x10 12 ions/cm 2 . At 100 MeV energy of O 7+ ion the electronic and nuclear energy loss for TiO2 film have been measured 7.38x10 -1 KeV/nm and 3.8x10 -4 KeV/nm respectively. However, the electronic and nuclear energy loss of ion irradiation for ITO substrate were 7.4x10 -1 KeV/nm and 4.06x10 -4 KeV/nm respectively. Similarly longitudinal/ lateral straggling of ITO and TiO2 have been found 3.87 μm/2.50 µm and 3.62 µm/1.14 μm respectively. Further, the structural and optical properties of these samples were monitored by X-ray diffraction (XRD), scanning electron microscopy (SEM) and UV-visible spectroscopy. It was found that oxygen ion (O 7